Recommended Posts

I've *never* had a problem with this before, and am a bit stumped as to what's happening...

I made a couple of handles yesterday out if 3/8" square hot rolled mild steel. Just finished wire brushing them (after a vinegar bath to remove scale), and noticed cracks along the edges of the twist.

I twist well into the oranges (and understand this stuff can be twisted cold), so I can't imagine that was an issue.

Again, I've never run into this with mild steel before. Any thoughts?

Alright, here we go with some photos.
IMG_1833-e1398961236952.jpg

IMG_1838-e1398961182914.jpg

Link to comment
Share on other sites

As Thomas noted, A36 is prone to all sorts of ailments due to the inconsistent nature of the melts.  The imported stuff is dreck. It is the 69 cent/pound hamburger (the other white meat  :blink:  ) of the steel world. Your batch may be high in copper, lead, sulfur, etc.

 

If you need quality, you have to specify the grade you want, such as 1018. Demand certs with each batch.

Link to comment
Share on other sites

Thanks guys. I suspect you're right.  I've been getting my steel from Metal Supermarkets, had run out of 3/8" and just restocked. I'm guessing they gave me whatever they had on hand.  Ah nuts! I've got 80' of this stuff to use up - and do a lot of twists with the smaller scale items like this. :-(

 

Well, lesson learned. I'll me more specific the next time I go shopping.

 

Cheers,

Neil

Link to comment
Share on other sites

hot rolled is a process;   this is not any type of grade or alloy.

A36 is a structural specification; not an alloy, and it can contain most anything as long as breakage and stretch limits are met.

1018 is an alloy; standards state what may and may not be conmtained in the melt.

 

sometimes we need to be reminded of that, and we need to remember when we order.

Link to comment
Share on other sites

Isn't it refreshing to be getting closer to the earlier days of the craft where a smith had to examine and test each new load of metal to know what they had and what it would be good for!

 

(Moxon mentions this in the 1703 edition of "Mechanics Exercises")

Link to comment
Share on other sites

Apparently, I didn't know to specify either.

So I happened to call over to my local Metals Supermarket this afternoon. Generally, their cold rolled is 1018 and their hot rolled is A36. Not sure the cost difference, but will certainly specify 1018 next time.

Link to comment
Share on other sites

Looks like low bid supplier steel to me.  It happens sometimes.  Cut it off, throw away, try again.  

 

Is there a locally owned and operated place you can buy steel?  Such a place may be more sympathetic when you bring your workpiece to them and say "This steel is c#$p."

Link to comment
Share on other sites

As noted not really that suitable for what you are using it for, however it really should be good for another smithing project so get what will work for your twists and you will have an inventory of stock for the other projects that need 3/8 sq. If we had unlimited funds these problems would not bug us so much, but I sure try to not get more worked up than nessisary over stuff like this.

Link to comment
Share on other sites

Try reliving the corners a bit with a hammer, a file or grinder before twisting it. I find twisting cold with relived corners can sometimes eliminate the cracks. It might be worth the effort instead of chucking the stock in the scrap bin.

 

brad

Link to comment
Share on other sites

I'll break from everybody else, and bet it's your coal. I still have about 5 bags of otherwise fine bituminous, that without a careful coking , cracks my metal everytime. I keep it around to prove to people that, some times it really is the coal's fault........Take care, matt

Link to comment
Share on other sites

Lupiphile i do recall reading somewhere,maybe in one of my books that there were two different things that low grade coal could contain too high a content of,dont remember right off what they were but one could potentially cause the iron to become hot short and the other could make it cold short meaning it could fracture in the higher temp range or after it had cooled it could fracture.I will dig around later on and see if i can find it and if so will post the info.

Link to comment
Share on other sites

Most common causes of Hot Short/Cold Short is too much Sulfur and too much Phosphorus.  Cold shortness is a function of too much Phosphorus.  Hot shortness; aka red shortness is a function of too much sulfur.  You can have both present making the steel hard to work at any temperature!

 

Note that manganese is added to steel to help scavenge sulfur that may creep in through the smelting process using coke.

Link to comment
Share on other sites

We ran into this starting about two years ago when bending 1/2" square A36 into a u shape then flattened. We tried different techniques and finally came up with bending it at a lower temperature. We used to bend it at a bright red to low orange but started getting cracks that looked like yours. This was done in a gas forge, the same way for years. I could use 1018 cold rolled but the cost is at least three times the cost and I go through tons of it.

Link to comment
Share on other sites

first rule of blacksmithing,,, get it hot. when its
yellow its mellow, when its red its dead.

a very good Santa Fe smith had this written on all his hoods.

serious, here, if you are going to get to an orange, not hot enough, leave it in a few seconds longer, get it yellow, and only do it once.

Link to comment
Share on other sites

one more thing, yes it can be twisted cold but you are limited to the amount of twists per inch or it will crack or shear. at a yellow heat you can separate your look from that of the cold work guys and double or triple the amount of twist without cracking,,, no matter what kind of steel you use or how powerful your twister.

PLEASE NOTE! this is no critique for how you do your work, just adding info to a problem.

Link to comment
Share on other sites

first rule of blacksmithing,,, get it hot. when its
yellow its mellow, when its red its dead.

a very good Santa Fe smith had this written on all his hoods.

serious, here, if you are going to get to an orange, not hot enough, leave it in a few seconds longer, get it yellow, and only do it once.

When we got it over orange, into the yellow, it cracked worse. Getting it hotter doesn't work for the iron I'm getting any more. I guess I'm making new rules. This is for products I've been making for years.

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
×
  • Create New...