March 30, 201214 yr Looking to create a knife pocket clip. I see some people use titanium, what would be recommended thickness to be strong enough but not too obstrusive? It would need bending, anything to bear in mind if hot bending it?
March 30, 201214 yr Hot bending: it absorbs gasses and becomes brittle so keep it at temp as short a time as possible.