December 17, 201015 yr I have a couple of blocks of tool steel in my shop that I thought was S2. I was sending some other material out to be tested, and chopped off a piece of my "S2" to have it checked as well. Results came back as follows: Carbon: 0.60 % Manganese: 0.80 Phosphorus: 0.017 Sulfur: <0.005 Silicon: 2.09 Nickel: 0.12 Chromium: 0.23 Molybdenum: 0.34 Copper: 0.10 Aluminum: 0.01 Vanadium: 0.18 So, 50 percent more carbon, pretty much double all of the other normal S2 alloys (except for Moly), plus some vanadium. Is this really S2? If not, anyone have any idea what it actually is or how to heat treat it?
December 17, 201015 yr Looks pretty close to me, even the vanadium. S-2:C: 0.65-0.70%Si: 1.00-1.25%Mn: 0.45-0.60%P: 0.025% MaxS: 0.025% MaxCr: 0.10-0.30%Mo: 0.40-0.50%V: 0.15-0.25%Oh, it's you, David! Where'd you get your specs for S-2 from? As a side note AISI 9260 is a cheap substitute for S-2: Carbon, C 0.560 - 0.640 % Iron, Fe 96.085 - 96.89 % Manganese, Mn 0.750 - 1.00 % Phosphorous, P <= 0.0350 % Silicon, Si 1.80 - 2.20 % Sulfur, S <= 0.0400 %
December 17, 201015 yr Author Maybe I have the wrong specs for S2. I thought the specs were: Carbon 0.4 - 0.55 Manganese 0.3 - 0.5 Molybdenum 0.3 - 0.6 Phosphorus 0.03 max Silicon 0.9 - 1.2 Sulfur 0.03 max Vanadium 0.5 max Maybe the stuff is actually AISI 9260? Or perhaps this material varied more than I thought? As to where I got it, the material I asked about above, I got from Howard seven or eight years ago in exchange for a bunch of nice old wrought iron anchor chain. I've been looking, unsuccessfully, for S2 ever since, because it seemed like it would be a good material for swords. At Ric Furrer's suggestion, I e-mailed Aldo ( http://njsteelbaron.com/ ) a couple of months back, initially thinking that maybe he knew somebody who could do a small custom run. Miraculously, he was able to find me about 800 lbs of 3/4 inch round bar stock. Just had it tested, and it is indeed S2, so I'm a very happy guy. All I ahve to do now is heat it up and run it through my rolling mill, and presto, I'll have S2 blade stock! Anyways, thanks very much for the intel Grant.
December 18, 201015 yr Looks very close to S5. Close enough that it probably *is* S5. If you don't want it, I could probably be persuaded to take it off your hands. :)
December 26, 201015 yr Author Looks very close to S5. Close enough that it probably *is* S5. If you don't want it, I could probably be persuaded to take it off your hands. Sure enough, it looks like it's S5. Thanks Matt. I'd been heat treating this stuff as though it was S2, and getting cracks. (And not a very good temper line.) No wonder. Now that I know what it is, it should be fun to play with. Moral of the story, at least as far as I'm concerned, is, before investing dozens of hours forging, filing, heat treating, finishing, etc., always test to make sure you know what you're working with.
February 3, 201115 yr Moral of the story, at least as far as I'm concerned, is, before investing dozens of hours forging, filing, heat treating, finishing, etc., always test to make sure you know what you're working with. Amen David Ric
February 10, 201115 yr Sure enough, it looks like it's S5. Thanks Matt. I'd been heat treating this stuff as though it was S2, and getting cracks. (And not a very good temper line.) No wonder. Now that I know what it is, it should be fun to play with. how does tempering leave lines?
February 10, 201115 yr how does tempering leave lines? Tempering doesn't leave tempering lines. Differential hardening leaves temper lines. One of the many incongruities of the English language as mutated by marketing mahem. :blink:
Join the conversation
You can post now and register later. If you have an account, sign in now to post with your account.