Dan C Posted April 29, 2013 Author Share Posted April 29, 2013 If you're correct about them being induction hardened, what would the expected result be after forging, hardening & tempering? Similar to the results of using .45% carbon steel? Quote Link to comment Share on other sites More sharing options...
Dan C Posted April 29, 2013 Author Share Posted April 29, 2013 I don't know anything about induction hardening other than what I just read on wiki. Seems like you would loose the hardness and be back to whatever mild carbon steel it started out as after heating to a de-magnetized state and quenching. Quote Link to comment Share on other sites More sharing options...