Ric Furrer Posted June 16, 2011 Posted June 16, 2011 Hello All, I heard about this "safe" Superwool 607 HT ceramic fiber wool material so I bought some. It is rated at 1300C max and continuous at 1150C...I found it breaks down at my welding temps rather quickly and would say that general forging it would be just almost OK, but not for higher temp work. I'll try a satanite wash and see if that improves the life. I had been using it as an end cap to cover the forge ends and it got hard and melted at my welding temps. Ric Quote