Recommended Posts

It's made from 1340, Turned on a lathe, to be heat treated.
On the matter of selling any, I made it in my spare time during school from scrap. I don't think I could afford the steel, let alone ask a decent price for it. Also, won't have spare time on the lathes till the end of next semester.

Link to post
Share on other sites

Since this is a class project, if the heat treat is for class credit then go for it. If you need to figure the heat treat on your own then, after looking at the specs, don't worry about it. Also the specs seem to call for rather long soak times, so if your school does not have controlled heat treat ovens I would want to avoid it.

Very nice job. I hope you got a good grade.

Phil

Link to post
Share on other sites
  • 2 weeks later...

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

×
×
  • Create New...