I actually spoke wrong. I should have said T-Style. Im following your PDF this time. My first go around I did not have the confidence to try it, now I do. So the more I think about this the more I like it. I can easily get angle iron, and I'll purchase bricks, id bolt it as well. If I understand correctly I can easily convert this from 1 burner to 2 or even three just by adding firebricks and a burner. My concern is how well will this perform compared to kaowool, satanize, itc-100 liner? Any cons I'm not thinking about? will it reach forge welding temps given the correct cubic inch? Thanks for the response, I know not all tool will solve for everything. I only have enough for one solution currently and I am not sure when I will have more funds for another, so I am trying to pick the one that will allow me to do the most. If there are things I can not do with one then I dont do them and I wait. no biggie. Thing is, I not think I need a two burner, I feel it was a design error on my part. Im always having to heat so much metal just for the 4-5 inches I'm working on. So id like to move to a single burner, but with zero experience with a single burner I want to make sure I am not screwing myself over. Originally I was just going to make a single burner horizontal round with a style burner. Was curious if the vertical was better, I think that's more for small work like knives. I want to do scrolls and whatnot so I do need some space to fit my work in, thats why I was shying away from the vertical. The clamp together one has made me rethink my plans. Thanks again for your time
-
I was unable to find a way to edit my post :/ Ive also thought about building two burners and just using angle iron and firebricks to make a modular forge. How would heat retention and heat loss be? Would I get it up to forge welding temps? What are the cons of doing this way because the versatility is very attractive.
-
I know all of my questions have been answered hundreds of times before, its just I find 100 different answers. Question: Which forge and burner is the best all around forge? I first am stuck between a vertical or a horizontal. I *THINK* I could do casting with a vertical??? as for traditional horizontal, I think I have decided on a round one though Ive read the shape only matters for heat up, once the work goes in the shape does not matter anymore? Single burner or two? I think I built my first forge way to long. I also have a coal forge I built that I use also, this way I do have a backup plan for pieces that don't really fit in the propane forge. Then the burners, I think I've decided on building 1 or 2 T-REX burners as I hear they are the most fuel efficient. Any advice is greatly appreciated. What I forge: Im a hobbiest nothing more, I currently am forging fireplace tool sets, tongs, leafs and hooks, things like that.I want to someday forge a sword, but it won't be what I get excited over, I found I'm not as interested in making knives as I have been in making towel holders, banana holders, and more artistic things. Im not 100% sure what I want to do as I'm only a year in and still learning. Current Forge: My current forge is a two burner setup that is able to forge weld but I designed with several flaws. Now that my skill has evolved, my back burner has been acting up and become unusable. One of the flaws was I did not make it so it would be maintainable very well, welded instead of having a collar for mounting. So instead of messing around with it anymore I will build a new one. This one also uses a lot of fuel, I think, nothing to compare it to. forge - https://www.iforgeiron.com/topic/60383-first-gas-forge/ burners - https://www.youtube.com/watch?v=BjqA4VQMpiM Thanks for reading.
-
Would this work for flashback protection? [link removed] Heres a picture of the forge, the hose is about 14 inches from the burner. Does this look okay? Father of 4 here, need to make sure I'm here for them tomorrow so please help guide this total newb, I work at a desk so this world is very new to me. Edit: Also will only be working with the garage door open, so I think I'm okay for ventilation and co gas.
-
The Rigidizer I am using is instuff. I don't think I will be firing the forge up until I get to the Satanite layer. I will wait 24 hours in between layers of instuff.
-
lol yeah i know, english is hard the welds on my forge would have been a better phrase Thanks for the response, ill do as you recommend.
-
As hard as it was, I ordered more and waited. Im now about to put the first layer of wool in today, im going to apply rigidizer to both layers of wool, is this correct? Do I coat both sides of the wool ( the whole blanket) with rigidizer or just the inside side? Im only two week into learning to weld so my forge welds are not air tight, i worry about fibers making it through my welds which is why I wonder if I should coat the outside of the blanket also.
-
Thank you for the advice. I ended up not ordering enough inswool :-/. So would it be just as good if I line the floor with firebrick, the sides and top with the inwool, and coating the firebricks with the Satanite, ITC-100 and bubble alumina? Or should I just order what I need and wait patiently?
-
Thank you for your response. The thread tape I used says "yellow gasoline". Is that the correct stuff or is there special stuff for propane?
-
So I will mount the flange 1in or so into the case, halfway into the liner, do I coat the holes with everything or just a Rigidizer? Want to make sure there is no way for the fibers to kill me Also I did use yellow tape on all my threads for the burners. Frosty said this is dangerous? Isn't that what its for though?
-
Very new to metal working so please guide me if this sounds stupid or I sound like I have no clue what I'm talking about (this is the case, this is all very very foreign to me) I welded a metal box 9x12x15 Tomorrow when I get all the lining stuff I will begin the following. two one inch layers of inswool coat with Instuff Ceramic-Fiber Rigidizer add a layer of Satanite Refractory Mortar coat with ITC-100 Refractory Coating then a layer of bubble alumina for the floor. when all is done I plan on 5x8x15 for a chamber of 600 cubic inches. I made two of these burners https://www.youtube.com/watch?v=BjqA4VQMpiM My main question I am trying to answer is how "deep" do I mount the burners? The end where the flame comes out should that be mounted flush with the insulation at the chamber or do I mount it flush to the metal frame and the flame pass through a hole drilled in the insulation. Do I coat the holes in the inswool with all the coatings?