Everything posted by Conrad.blacksmithing
-
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
No insults taken jlp. I think it's cool that you are able to apply different methods to different processes. I just like punching and getting plugs. It give a sense of reward almost for punching a nice clean plug. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
I lose hardly any weight to the plug. In fact I lose more weight in scale than the plug. 1/4 oz at the most... -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
It's a punch but not with a flat bottom if that's what you're asking. It has a bevel to punch easier. I don't go all the way through one side. I go through about 3/4 of the billet then flip. This results in a much cleaner hole. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Good work everybody! You guys are killing it. Finished a new hammer eye punch for myself because my dad broke the last one lol. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Yes that's a good answer too. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
You could be right. It could centralize the impact. I'm sure there are a million reasons, as with everything! -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
That's a great question. I don't think that there is any special purpose for them because a hammer without fullers would probably perform just as good. They are mostly for looks just to give the hammer more character. Maybe someone has a reason for them but that's what I think. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Thanks jlp. Its my goal to keep the forging on my tools as clean as possible. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Thanks Chris! -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Finished that ball peen today! I finally figured out how to keep the troughs shiny through heat treat. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Yeah I'll be talking about it for a while that's for sure. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
I like the pendant Rojo. The way it flows is pleasing to look at. Tongs take a lot of practice to perfect. I've been making them from a while and still struggle! Today I made some tooling for bull dog keychains and my first bull dog. Also forged a 2.5lb ball peen for a machinist customer. I also had a punch break in a crazy way. I've never seen a top tool break like this. My dad hits like a power hammer! -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Unfortunately (but really fortunately) most of the people around me are elder. It is really is quite easy to break up the coal. Plus I'm used to chopping wood all day for the forge. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
I finished unloading a massive load of coal I recently acquired for $150. Just under 4 yards (8,000lbs). Super excited because this is going to save me a lot of money. -
Thanks for the info, Glenn! I personally love Hay Budden anvils.
-
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
I posted them on Instagram. I don't have any dimensional pictures because it's already sold but I posted more. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
It turned out to be just under 2.75lbs. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Really like the bolster Goods! Super clean. Got another camp axe basically finished ( just have to do some more oiling). The hickory on this one is really appealing to me, very straight grain too. -
which anvil?
Conrad.blacksmithing replied to karcher.dc's topic in Anvils, Swage Blocks, and Mandrels
I would take the Hay in a heartbeat. I have a Vulcan and a Hay Budden and the Hay is far superior in face hardness, shape, and material quality. Vulcans had thin face plates and if that Hay was made after 1914 (which it looks like it may have been, maybe) it will have a full top half of solid tool steel. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Thanks! The faces are pretty evenly weighted. I have actually been surprised by how easy it is to balance these hammers. It's on the ground because I haven't mounted it yet. I like taking pictures on it so that's what I use (I'm also in love with Hay Budden) -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Progress on the candelabra is looking good JHCC. Got that 2.75lb square circle done after replacing the bearings on my belt sander. I think I like square circles more than classic rounding hammers. -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
It is 4140. I also figured out that 4140 likes a lower temper. This time I tempered it to around 410-425 F and it stayed a little harder (didn't dent the pole when hammered on cold steel). -
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Conrad.blacksmithing replied to Mark Ling's topic in Blacksmithing, General Discussion
Cool fire poker Billy! Looks like it could kill a cougar Yesterday I finished a 2.75 square circle hammer and made a flat chisel and eye punch. I tested the eye punch out on a horse head bottle opener and I think it looks good. Oh and I forged a new cupping tool.