Everything posted by Mark Ling
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Thanks guys! Actualy das you have me tempted cause I'm really not a fan of this hammer. I may give it to someone. Recently I have just really not been pleased with my work it's starting to get in my nerves. At then kinda like well if you don't like it should you sell it, give it away, keep it as a shop hammer, or scrap it. I already got a few in the scrap pile. -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
finished up this 20 oz hammer that I had forged a while back. I polished the faces to cover up a bad blow from a striker....I kinda like this style but not really at the same time. Littleblacksmith -
L brand coke buy it by the ton ships from Georgia its pretty affordable. Google it its what I use. Littleblacksmith
-
My first hot cut hardy
Mark Ling replied to Nhvalentine's topic in Hot Cuts, Anvil devils, metal cutting on the anvil.
Id normalize that edge. 4140 Will hold up just fine against hot steel, and leaving it hardened and tempered runs the risk of damaging your hammer face or taking a chip out of the hot cut. Littleblacksmith -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
JHCC if you don't like the finish on it than why wouldn't you fix it? personally I would fix it so I would be pleased but that's just cause I find if I don't like something I made I either fix it or get rid of it. Only other recommendation is to bring that grid back a bit for a thinner edge. Littleblacksmith -
Show me your Bottle Openers!
Mark Ling replied to Arbalist's topic in Blacksmithing, General Discussion
Thanks y'all. Littleblacksmith -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
thank you Ranchmanben! Aus, thank you. Haha I've never had any comments other than oh those are cool, maybe its just a location difference. I have forged craftsmen and snap on before. Yes I said snap on. I get them at the scrap yard, and I already have more wrenches than I need and so I just look at it that before I got them they were just gunna be thrown away and melted down so I'm doing them a favor for actually doing something more meaningful with them. I hang on to the old ford wrenches though that I find I dont forge them. Littleblacksmith -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Thanks guys. Littleblackmith -
Show me your Bottle Openers!
Mark Ling replied to Arbalist's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Thank you Mr. Hewitt and Mr. Richter! Thanks agian Jlp! Thank you Cincinnatus! So today I finished that 3.5lb hammer, ready to be shipped out. here is a better picture. -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Thank you jlp! Not sure It was more professional than you, you have a pretty nice set up. Thanks Ben! Yes sales were good sold a bit over $800 of stuff. Littleblacksmith -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Wasn't done in the shop, but actually at an event that a friend and I were selling at and demoing at. While there we forged this 3.5lb hammer and some other stuff. Ended up having to stop early cause of weather but did well at the show. The hammer we finished the quickest we have ever, took about an hour and a half. Next to it is the starting billet. Littleblacksmith Here is some pictures from the show and demo. -
I have had some issuers when I don't put a metal wedge that the wood wedge will come out, so I now always do a metal wedge it's a very small metal wedge, about half or less the size of the store bought ones. It's big enough it wedges the wedge in, but doesn't typically split the handle any. I imagine soaking the head may help with that though. Littleblacksmith
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Nice hammer. Littleblacksmith -
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
Colorado cj- the leaves are looking good, and the stems are looking very good. Good job. -
I just saw your latest reply JHCC. Yes, apologies, it was my bad I should've not used the word force. Thank you, you're doing good also. I still have a long ways to go till I would say that I am good at it though. Thanl you buzzkill! Well if you are ever near me give me a shout and I'll show you my shop, that goes for anybody. That was all very nice if you to say. Littleblacksmith Yes JHCC that would be very interesting. Who knows, maybe it does hit as fast as a hand hammer and it just looks like it doesn't cause it's so big. Dunno.
-
Oh boy. I had just meant that it seems to take about the same amount of heats as it would with a hand hammer, I shouldn't have said force. Yes I think if you could have the treadle hammer accelerate just as fast as a hand hammer it would be golden, but I don't think ive ever seen a foot powered treadle hammer hit as fast as a hand hammer. I'm sure it does have its place though, would be handy for using tooling. I was about to buy one this last February. The treadle hammer had more mass but slower speed is the difference. I think.......... I'm no physics teacher though. Littleblacksmith
-
What did you do in the shop today?
Mark Ling replied to Mark Ling's topic in Blacksmithing, General Discussion
JLP- I was at school, and I realized, I reckon i do draw a little. Maybe not at times when I should be but I do draw some. Here is a page in a packet we got in english about the state wide writing test, I did some drawing. That's how most of my notes and papers look haha. I do like the cross pein style I drew and wanna try it out sometime soon. Thanks Steam boat! Littleblacksmith