i may be able to picturize in my mind what you are telling.
Thank you for assisting. i may text you again in case i require further assistance.
Using Induction heating, the problem arises due to inaccurate bending technique.
No, no hardening/tempering/quenching process is done.
Looks like you are familiar with the product. i may be texting you later in case i am stuck at any step .Thanks for your help.
So basically i need to try and push the bend from outside ? i am familiar with forming presses and might have and idea of what you say.
Thank You
and this will be produced in higher amounts if successfully developed.
Yes it is the process we use.
Forging part is done.The problem occurs in the bending part. Since i need high precision.
And its a risk we have to take by spending some time and exploring the market.
Welding would not do the job .
But Thank you for your help.