(((make it WELD (not just stick)??)))
I may be taking this way too literally, but the short answer is NO. If you get the steel hot enough to *weld* the brass will probably be long gone. Brass will adhere to the surface of the steel. Minute scratches and surface blemishes allow the brass a better grip, but it won't weld or mix in a homogeneous blend. That's according to the way I interpret the question.
Like I said, I tend to take some things way too literally.
|